MIL-DTL-14072F
TABLE VII. Finish selection - continued.
Applicable Finish 1/
Class of Part
Conditions Affecting
Type
Finish Selection
Exposure
FABRICATED FROM ZINC-BASE ALLOYS
All parts
None
I
P611.1, P611.2, P613.1
or P613.2
Part is small and
I
M611
painting is not
practical.
Painting is desired or
II
P615.1, P615.2 +P611.1,
required to provide a
P611.2, +P613.1 or
nonconducting
+P613.2
surface.
Parts will be
II
M611 or any paint finish
subjected to
per Table I
temperatures in
excess of 71°C.
Parts will not be
I
E611
subjected to
temperatures in
excess of 71°C.
Parts will be painted
I
E611 or E612
after assembly.
Parts have prior
I
P371.1 or P371.2
finish (E611 or E612)
and require painting.
PARTS FABRICATED FROM MAGNESIUM-BASE ALLOYS
All parts fabricated from
None
I and II
See Table I.
zinc-bearing magnesium
alloys.
All parts except those
None
I and II
See Table I.
subject to flexing
All parts except those
None
I and II
See Table I.
containing zinc.
FABRICATED FROM WOOD
All parts and assemblies
None
I or II
P911
1/ Allowable basic paint finishes (steps 1 through 3 of Table I) are prefixed with +, for
example +P211. When no + is shown, it is understood that complete finishes (steps 1
through 4 of Table I) are required and finish call-out shall include the letter
designation of the final film, for example P211A.
57